Gong J.J., Lin C.J.
Xiamen University, CN
Keywords: water-splitting
In order to further enhance photoeletrocatalytic reactivity, it is desirable to develop a facile and effective technique to obtain high quality Pd@TNTAs with homogeneous dispersion and small enough particle size down to few of nm Pd quantum dots (QDs) on the geometrically-ordered TiO2 nanotube arraysIn this paper we report an investigation on the Pd QDs sensitized TiO2 nanotube arrays (Pd/TiO2NTs) and their excellent performance in hydrogen production by photoelectrocatalytic water splitting. The Pd QDs are found uniformly distributed on both inside and outside TiO2 nanotubes with average size from ~2.5 to ~4nm with a very narrow size distribution. Uniform coverage of Pd QDs from the pore bottom to top has been achieved. The obtained nanocomposites showed an incident photon-to-current conversion efficiency (IPCE) value of nearly 100% and a significantly enhanced photocatalytic hydrogen generation rate of about 592 mmol•h-1•cm-2 under 320 mW/cm2 irradiation. These results clearly demonstrate that Pd QDs sensitized TiO2 nanotube arrays can remarkably improve the photocatalytic efficiency.
Journal: TechConnect Briefs
Volume: Technical Proceedings of the 2011 Clean Technology Conference and Trade Show
Published: June 13, 2011
Pages: 399 - 402
Industry sectors: Advanced Materials & Manufacturing | Energy & Sustainability
Topic: Catalysis
ISBN: 978-1-4398-8189-7